Carbon nanostructures of different kinds have been synthesized by chemical vapor deposition. By modifying the deposition temperature, the catalyst material, and the hydrocarbon, nanofibers with herringbone structure, multi-walled nanotubes with tubular structure, and single-walled nanotubes were deposited. The nanostructures were purified with different treatment methods. The carbon nanostructures were characterized using scanning and transmission electron microscopy. The hydrogen storage capability was investigated for all obtained nanostructures. The measurements show that the storage capacity of hydrogen is very limited in all the carbon nanostructures.

Bubble dynamics, including the formation, growth, and detachment, of single H2 bubbles was studied at a platinum microelectrode during the electrolysis of 1 M H2SO4 electrolyte. The bubbles were visualized through a microscope by a high-speed camera. Electrochemical measurements were conducted in parallel to measure the transient current. The periodic current oscillations, resulting from the periodic formation and detachment of single bubbles, allow the bubble lifetime and size to be predicted from the transient current. A comparison of the bubble volume calculated from the current and from the recorded bubble image shows a gas evolution efficiency increasing continuously with the growth of the bubble until it reaches 100%. Two different substrates, glass and epoxy, were used to embed the Pt wire. While nearly no difference was found with respect to the growth law for the bubble radius, the contact angle differs strongly for the two types of cell. Data provided for the contact point evolution further complete the image of single hydrogen bubble growth. Finally, the velocity field driven by the detached bubble was measured by means of PIV, and the effects of the convection on the subsequent bubble were evaluated.

Analytical expressions for the anodic stripping voltammetry of metallic nanoparticles from an electrode are provided. First, for reversible electron transfer, two limits are studied: that of diffusionally independent nanoparticles and the regime where the diffusion layers originating from each particle overlap strongly. Second, an analytical expression for the voltammetric response under conditions of irreversible electron transfer kinetics is also derived. These equations demonstrate how the peak potential for the stripping process is expected to occur at values negative of the formal potential for the redox process in which the surface immobilised nanoparticles are oxidised to the corresponding metal cation in the solution phase. This work is further developed by considering the surface energies of the nanoparticles and its effect on the formal potential for the oxidation. The change in the formal potential is modelled in accordance with the equations provided by Plieth [J. Phys. Chem., 1982, 86, 3166-3170]. The new analytical expressions are used to investigate the stripping of silver nanoparticles from a glassy carbon electrode. The relative invariance of the stripping peak potential at low surface coverages of silver is shown to be directly related to the surface agglomeration of the nanoparticles.