Helen C. Cox

Injectable scaffolds are of interest in the field of regenerative medicine because of their minimally invasive mode of delivery. For tissue repair applications, it is essential that such scaffolds have the mechanical properties, porosity and pore diameter to support the formation of new tissue. In the current study, porous poly(dl-lactic acid-co-glycolic acid) (PLGA) microspheres were fabricated with an average size of 84±24μm for use as injectable cell carriers. Treatment with ethanolic sodium hydroxide for 2min was observed to increase surface porosity without causing the microsphere structure to disintegrate. This surface treatment also enabled the microspheres to fuse together at 37°C to form scaffold structures. The average compressive strength of the scaffolds after 24h at 37°C was 0.9±0.1MPa, and the average Young's modulus was 9.4±1.2MPa. Scaffold porosity levels were 81.6% on average, with a mean pore diameter of 54±38μm. This study demonstrates a method for fabricating porous PLGA microspheres that form solid porous scaffolds at body temperature, creating an injectable system capable of supporting NIH-3T3 cell attachment and proliferation in vitro.

The development of growth factor delivery strategies to circumvent the burst release phenomenon prevalent in most current systems has driven research towards encapsulating molecules in resorbable polymer matrices. For these polymer release techniques to be efficacious in a clinical setting, several key points need to be addressed. This present study has investigated the encapsulation of the growth factor, BMP-2 within PLGA/PLGA-PEG-PLGA microparticles. Morphology, size distribution, encapsulation efficiency and release kinetics were investigated and we have demonstrated a sustained release of bioactive BMP-2. Furthermore, biocompatibility of the PLGA microparticles was established and released BMP-2 was shown to promote the differentiation of MC3T3-E1 cells towards the osteogenic lineage to a greater extent than osteogenic supplements (as early as day 10 in culture), as determined using alkaline phosphatase and alizarin red assays. This study showcases a potential BMP-2 delivery system which may now be translated into more complex delivery systems, such as 3D, mechanically robust scaffolds for bone tissue regeneration applications.

Biodegradable polymer scaffolds have great potential for regenerative medicine applications such as the repair of musculoskeletal tissues. Here, we describe the development of scaffolds that blend hydrogel components with thermoplastic materials, combining the unique properties of both components to create mouldable formulations. This study focuses on the structural and mechanical properties of the composite scaffolds, produced by combining temperature-sensitive poly(DL-lactic acid-co-glycolic acid) (PLGA)/poly(ethylene glycol) (PEG) particles with a hydrogel component [Pluronic F127, fibrin or hyaluronic acid (HyA)]. The composite formulations solidified over time at 37°C, with a significant increase (p ≤ 0.05) in compressive strength observed from 15 min to 2 h at this temperature. The maximum compressive strength was 1.2 MPa for PLGA/PEG-Pluronic F127 scaffolds, 2.4 MPa for PLGA/PEG-HyA scaffolds and 0.6 MPa for PLGA/PEG-fibrin scaffolds. Porosity for each of the PLGA/PEG-hydrogel formulations tested was between 50 and 51%. This study illustrates the ability to combine this thermoplastic PLGA/PEG system with hydrogels to fabricate composite scaffolds, and demonstrates that altering the particle to hydrogel ratio produces scaffolds with varying mechanical properties.

There is a need to control the spatio-temporal release kinetics of growth factors in order to mitigate current usage of high doses. A novel delivery system, capable of providing both structural support and controlled release kinetics, has been developed from PLGA microparticles. The inclusion of a hydrophilic PLGA-PEG-PLGA triblock copolymer altered release kinetics such that they were decoupled from polymer degradation. A quasi zero order release profile over four weeks was produced using 10% w/w PLGA-PEG-PLGA with 50:50 PLGA whereas complete and sustained release was achieved over ten days using 30% w/w PLGA-PEG-PLGA with 85:15 PLGA and over four days using 30% w/w PLGA-PEG-PLGA with 50:50 PLGA. These three formulations are promising candidates for delivery of growth factors such as BMP-2, PDGF and VEGF. Release profiles were also modified by mixing microparticles of two different formulations providing another route, not previously reported, for controlling release kinetics. This system provides customisable, localised and controlled delivery with adjustable release profiles, which will improve the efficacy and safety of recombinant growth factor delivery.