Determining the bonding–degradation trade-off at heterointerfaces for increased efficiency and stability of perovskite solar cells
Jinxi Chen(National University of Singapore), Yi Hou(Hengyang Normal University), Wan Ru Leow(Nanyang Technological University), Zhuojie Shi(National University of Singapore), Shibo Xi(Agency for Science, Technology and Research), Hou Yi Chia(National University of Singapore), Donny Lai(National University of Singapore), Zhenrong Jia(National University of Singapore), Renjun Guo(National University of Singapore), Xiao Guo(National University of Singapore), Jia Li(National University of Singapore), Yuduan Wang(National University of Singapore), Zhenxiang Xing(Agency for Science, Technology and Research), Qi‐Lin Zhou(Nankai University), Xinxing Yin(Nanjing University of Science and Technology), Shunchang Liu(Chinese Academy of Sciences), Mingsheng Zhang(Howard Hughes Medical Institute), Xi Wang(National University of Singapore), Wentao Yan(National University of Singapore), Tao Wang(National University of Singapore), Haoming Liang(National University of Singapore)
Cited by 34
Related Papers
Managing grains and interfaces via ligand anchoring enables 22.3%-efficiency inverted perovskite solar cells
|Nature Energy|2020|1.2k
Bipolar-shell resurfacing for blue LEDs based on strongly confined perovskite quantum dots
|Nature Nanotechnology|2020|811
Efficient tandem solar cells with solution-processed perovskite on textured crystalline silicon
|Science|2020|770