Magnetic properties and structural characterization of layered (Cr0.5Mn0.5)2AuC synthesized by thermally induced substitutional reaction in (Cr0.5Mn0.5)2GaC
Chung‐Chuan Lai(Linköping University), Johanna Rosén(Linköping University), Jun Lu(Linköping University), Andrejs Petruhins(Linköping University), Michael Farle(University of Duisburg-Essen), Quanzheng Tao(Linköping University), Hossein Fashandi(Linköping University), Ruslan Salikhov(Helmholtz-Zentrum Dresden-Rossendorf), Lars Hultman(Linköping University), Per Eklund(Linköping University), Ulf Wiedwald(Universität Ulm)
Cited by 37
Related Papers
A general Lewis acidic etching route for preparing MXenes with enhanced electrochemical performance in non-aqueous electrolyte
|Nature Materials|2020|1.6k
Element Replacement Approach by Reaction with Lewis Acidic Molten Salts to Synthesize Nanolaminated MAX Phases and MXenes
|Journal of the American Chemical Society|2019|1.5k
Journal of Magnetism and Magnetic Materials
|Zenodo (CERN European Organization for Nuclear Research)|2022|955
Ferromagnetic resonance of ultrathin metallic layers
|Reports on Progress in Physics|1998|908
Two-dimensional Mo1.33C MXene with divacancy ordering prepared from parent 3D laminate with in-plane chemical ordering
|Nature Communications|2017|760