Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
Alisa Stratulat(University of Oxford), T.J. Marrow(University of Oxford), Jonathan Duff(University of Manchester)