The performance of perovskite solar cells with inverted polarity (p-i-n) is still limited by recombination at their electron extraction interface, which also lowers the power conversion efficiency (PCE) of p-i-n perovskite-silicon tandem solar cells. A MgF x interlayer with thickness of ~1 nanometer at the perovskite/C 60 interface favorably adjusts the surface energy of the perovskite layer through thermal evaporation, which facilitates efficient electron extraction and displaces C 60 from the perovskite surface to mitigate nonradiative recombination. These effects enable a champion open-circuit voltage of 1.92 volts, an improved fill factor of 80.7%, and an independently certified stabilized PCE of 29.3% for a monolithic perovskite-silicon tandem solar cell ~1 square centimeter in area. The tandem retained ~95% of its initial performance after damp-heat testing (85°C at 85% relative humidity) for >1000 hours.

Perovskite/silicon tandem solar cells offer a promising route to increase the power conversion efficiency of crystalline silicon (c-Si) solar cells beyond the theoretical single-junction limitations at an affordable cost. In the past decade, progress has been made toward the fabrication of highly efficient laboratory-scale tandems through a range of vacuum- and solution-based perovskite processing technologies onto various types of c-Si bottom cells. However, to become a commercial reality, the transition from laboratory to industrial fabrication will require appropriate, scalable input materials and manufacturing processes. In addition, perovskite/silicon tandem research needs to increasingly focus on stability, reliability, throughput of cell production and characterization, cell-to-module integration, and accurate field-performance prediction and evaluation. This Review discusses these aspects in view of contemporary solar cell manufacturing, offers insights into the possible pathways toward commercial perovskite/silicon tandem photovoltaics, and highlights research opportunities to realize this goal.

To achieve the full potential of monolithic perovskite/silicon tandem solar cells, crystal defects and film inhomogeneities in the perovskite top cell must be minimized. We discuss the use of methylenediammonium dichloride as an additive to the perovskite precursor solution, resulting in the incorporation of in situ–formed tetrahydrotriazinium (THTZ-H + ) into the perovskite lattice upon film crystallization. The cyclic nature of the THTZ-H + cation enables a strong interaction with the lead octahedra of the perovskite lattice through the formation of hydrogen bonds with iodide in multiple directions. This structure improves the device power conversion efficiency (PCE) and phase stability of 1.68 electron volts perovskites under prolonged light and heat exposure under 1-sun illumination at 85°C. Monolithic perovskite/silicon tandems incorporating THTZ-H + in the perovskite photo absorber reached a 33.7% independently certified PCE for a device area of 1 square centimeter.